Modification of Fe/Cu multilayers under 400 keV Xe<SUP>20+ </SUP>irradiation

WEI Kong-Fang; WANG Zhi-Guang; LIU Chun-Bao; ZANG Hang; YAO Cun-Feng; SHENG Yan-Bin; MA Yi-Zhun; SONG Yin; LU Zi-Wei

Chinese Physics C> 2008, Vol. 32> Issue(S2) : 262-264

Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation

Abstract
HTML
Reference
Related

PDF

Abstract：
Two kinds of Fe/Cu multilayers with different modulation wavelength were deposited on cleaved Si(100) substrates and then irradiated at room temperature using 400 keV Xe²⁰⁺ in a wide range of irradiation fluences. As a comparison, thermal annealing at 300—900℃ was also carried out in vacuum. Then the samples were analyzed by XRD and the evolution of crystallite structures induced by irradiation was investigated. The obtained XRD patterns showed that, with increase of the irradiation fluence, the peaks of Fe became weaker, the peaks related to Cu-based fcc solid solution and Fe-based bcc solid solution phase became visible and the former became strong gradually. This implied that the intermixing at the Fe/Cu interface induced by ion irradiation resulted in the formation of the new phases which could not be achieved by thermal annealing. The possible intermixing mechanism of Fe/Cu multilayers induced by energetic ion irradiation was briefly discussed.

References

[1]

. Pepperho W, Acet M. Constitution and Magnetism ofIron and its Alloys. Berlin: Springer-Verlag, 20012. Khmelevskyi S, Mohn P. Phys. Rev. B, 2005, 71: 1444233. Hansen M. Constitution of Binary Alloys. New York:McGraw-Hill, 19584. Yavari A R, Desre P J, Benameur T. Phys. Rev. Lett., 1992,68(14): 2235-22385. Harris V G, Kemner K M, Das B N et al. Phys. Rev. B,1996, 54(10): 6929-69406. LI T, LI Y Z, ZHANG Y H et al. Phys. Rev. B, 1995, 52(2): 1120-11227. LIU B X, ZHANG Z J. J. Phys.: Condens. Matter, 1996,8: 165-1718. CAI M, Veres T, Roorda S et al. J.Appl. Phys., 2004, 95(4):1996-20059. Amirthapandian S, Panigrahi B K, Srivastava A K et al.Nucl. Instrum. Methods B, 2003, 212: 140-14510. WEI L C, Averback R S. J. Appl. Phys., 1997, 81(2): 613-62311. LIU B X, LAI W S, ZHANG Q. Mater. Sci. Eng.R-Reports,2000, 29(1-2): 1-4812. WEI S Q, YAN W S, LI Y Z et al. Physica B, 2001, 305:135-142

[1]	YANG Yan-Ji , LU Jing-Bin , WANG Yu-Sa , CHEN Yong , XU Yu-Peng , CUI Wei-Wei , LI Wei , LI Zheng-Wei , LI Mao-Shun , LIU Xiao-Yan , WANG Juan , HAN Da-Wei , CHEN Tian-Xiang , LI Cheng-Kui , HUO Jia , HU Wei , ZHANG Yi , LU Bo , ZHU Yue , MA Ke-Yan , WU Di , LIU Yan , ZHANG Zi-Liang , YIN Guo-He , WANG Yu . Proton irradiation effect on SCDs. Chinese Physics C, 2014, 38(8): 086004. doi: 10.1088/1674-1137/38/8/086004
[2]	M. K. Suleymanov , K. H. Khan , A. Zaman . Study of the behavior of the nuclear modification factor in freeze-out state. Chinese Physics C, 2013, 37(2): 024101. doi: 10.1088/1674-1137/37/2/024101
[3]	WANG Fang-Fang , ZHU Jing-Tao , ZHONG Qi , WANG Zhan-Shan , Philippe Jonnard , Karine Le , Michel Andr , Michel Fialin . Influence of working gas pressure on the performance of W/Si multilayers. Chinese Physics C, 2012, 36(9): 909-914. doi: 10.1088/1674-1137/36/9/021
[4]	CHENG Jin-Xia , ZHANG Dong-Hai , YAN Shi-Wei , LI Jun-Sheng , WANG Li-Chun , LI Yan-Jing . The fragmentation of ²⁰Ne at 400 A MeV. Chinese Physics C, 2012, 36(1): 37-42. doi: 10.1088/1674-1137/36/1/006
[5]	XU Xiao-Ming , ZHOU Jie . Nuclear modification factor for J/ψ production in nucleus-nucleus collisions. Chinese Physics C, 2011, 35(5): 463-466. doi: 10.1088/1674-1137/35/5/011
[6]	ZUO Yi , ZHENG Yong-Nan , ZHOU Dong-Mei , YUAN Da-Qing , LIU Meng , FAN Ping , CUI Bao-Qun , MA Ying-Jun , LI Li-Qiang , LI Ji-Zhou , ZHU Sheng-Yun . PAC investigation of qudropole interaction in nano-soft magnetic material Fe_73.5Cu₁Nb₃Si_13.5B₉. Chinese Physics C, 2008, 32(S2): 259-261.
[7]	LI Rui-Qi , LI Chun-Dong , HE Shi-Yu , DI Ming-Wei , YANG De-Zhuang . Energy Transfer of keV Proton in Kapton/Al. Chinese Physics C, 2007, 31(1): 114-118.
[8]	WEN Wan-Xin , YANG Sheng-Sheng , WANG Li . XPS Study of Property Changes of The Themal Control Coatings with 110keV Proton Irradiation. Chinese Physics C, 2006, 30(4): 364-367.
[9]	WEN Wan-Xin , YANG Sheng-Sheng , WANG Li . Efsects of 110keV Proton Irradiation on Thermal Property of Themal Control Coatings. Chinese Physics C, 2006, 30(3): 268-272.
[10]	AN Yu-Kai , DAI Bo , MAI Zhen-Hong , CAI Jian-Wang , WU Zong-Hua . Elemental distribution at the interfaces of Ni₇₀Co₃₀/Cu magnetic multilayers by X-ray anomalous scattering. Chinese Physics C, 2005, 29(S1): 16-19.
[11]	YUAN Shi-Bin , WEI Zeng-Quan , LI Wen-Jian , GAO Qing-Xiang . Research on Molecular Modification of L(+)-Cysteine Induced by 110 keV Fe⁺ Ion Beam Irradiation. Chinese Physics C, 2003, 27(5): 460-464.
[12]	LI Long , ZOU Bing-Song , LI Guang-Lie . On the Nature of f₀(400-1200). Chinese Physics C, 2002, 26(4): 346-353.
[13]	TAN Wei-Shi , YOU Biao , ZHANG Jie-Qiu , WU Xiao-Shan , HU An , JIANG Shu-Sheng , WANG Jun , JIA Quan-Jie , ZHANG Wen-Li , JIANG Xiao-Ming . Magnetoresistance and Structural Studies on Co/Cu Multilayers with the Combination of the first and Second Antiferromagnetic Oscillation Peak. Chinese Physics C, 2001, 25(S1): 106-109.
[14]	Wu Dingqing , Li Wenxin , Sun Tongyu , Sun Rulin , Zhao Lili , Zhang Fengshou , Yin Xinmin , Jin Genming , Li Ze , Jing Kexing , Li Xinhua . Study of Recoil Properties of Target Residues From the Interaction of Copper With 20─46MeV/u ¹²C Ions. Chinese Physics C, 1996, 20(1): 13-20.
[15]	Liu Zhong , Sun Xiangfu , Zhou Xiaohong , Lei Xiangguo , Jin Hanjuan , Guo Yingxiang , Pan Qiangyan , Zhang Yuhu , Chen Xinfeng , Luo Yixiao , Wen Shuxian , Yuan Guanjun , Li Guangsheng , Yang Chunxiang . Identification of Excited States in ¹¹⁷Xe. Chinese Physics C, 1995, 19(S1): 1-4.
[16]	Liu Zhong , Sun Xiangfu , Zhou Xiaohong , Lei Xiangguo , Jin Hanjuan , Guo Yingxiang , Pan Qiangyan , Zhang Yuhu , Chen Xinfeng , Luo Yixiao , Wen Shuxian , Yuan Guanjun , Li Guangsheng , Yang Chunxiang . Identification of Excited States in ¹¹⁷Xe. Chinese Physics C, 1995, 19(2): 106-109.
[17]	CHEN Zhiqian . Binding Strength and Oxygen Coordination of the Fe Sites in High T_C GdBa₂ Cu₃O_7—δ. Chinese Physics C, 1993, 17(11): 971-975.
[18]	Chen Zhiqian . Binding Strength and Oxygen Coordination of the Fe Sites in High T_c GdBa₂Cu₃O_7-δ. Chinese Physics C, 1993, 17(S3): 225-229.
[19]	SHEN WEN-QING . NEUTRON RICH ISOTOPES ⁵⁴Ti, ⁵⁶V, ⁵⁷V, ⁵⁸Cr PRODUCED IN BOMBARDMENT OF ⁵⁶Fe TARGET WITH 79OMeV ¹³⁶Xe IONS. Chinese Physics C, 1982, 6(4): 462-465.
[20]	. A HIGH GRADIENT 250keV PULSED PROTON BEAM ACCELERATING EQUIPMENT. Chinese Physics C, 1981, 5(6): 722-731.

Access

Get Citation

WEI Kong-Fang, WANG Zhi-Guang, LIU Chun-Bao, ZANG Hang, YAO Cun-Feng, SHENG Yan-Bin, MA Yi-Zhun, SONG Yin and LU Zi-Wei. Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation[J]. Chinese Physics C, 2008, 32(S2): 262-264.

RIS(for EndNote,Reference Manager,ProCite)

BibTex

Txt

Milestone

Received: 2008-07-17
Revised: 1900-01-01

Article Metric

Article Views(3088)
PDF Downloads(619)
Cited by(0)

Policy on re-use

To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation

Corresponding author: WEI Kong-Fang,

Received Date: 2008-07-17

Accepted Date: 1900-01-01

Available Online: 2008-01-03

Abstract: Two kinds of Fe/Cu multilayers with different modulation wavelength were deposited on cleaved Si(100) substrates and then irradiated at room temperature using 400 keV Xe²⁰⁺ in a wide range of irradiation fluences. As a comparison, thermal annealing at 300—900℃ was also carried out in vacuum. Then the samples were analyzed by XRD and the evolution of crystallite structures induced by irradiation was investigated. The obtained XRD patterns showed that, with increase of the irradiation fluence, the peaks of Fe became weaker, the peaks related to Cu-based fcc solid solution and Fe-based bcc solid solution phase became visible and the former became strong gradually. This implied that the intermixing at the Fe/Cu interface induced by ion irradiation resulted in the formation of the new phases which could not be achieved by thermal annealing. The possible intermixing mechanism of Fe/Cu multilayers induced by energetic ion irradiation was briefly discussed.

HTML

Reference (1)

Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation

Abstract：

References

Access

Article Metrics

Metrics

通讯作者: 陈斌, bchen63@163.com

Email This Article

Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation

Corresponding author: WEI Kong-Fang,

HTML

目录

Modification of Fe/Cu multilayers under 400 keV Xe20+ irradiation

Abstract：

References

Access

Article Metrics

Metrics

通讯作者: 陈斌, bchen63@163.com

Email This Article

Modification of Fe/Cu multilayers under 400 keV Xe20+ irradiation

Corresponding author: WEI Kong-Fang,

HTML

目录

Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation

Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation