XPS Study of Property Changes of The Themal Control Coatings with 110keV Proton Irradiation

WEN Wan-Xin; YANG Sheng-Sheng; WANG Li

Chinese Physics C> 2006, Vol. 30> Issue(4) : 364-367

XPS Study of Property Changes of The Themal Control Coatings with 110keV Proton Irradiation

Department of Radiation Medicine, Soochow University, Suzhou 215007, China2 National Key Lab. of Vacuum & Cryogenics Technology and Physics, Lanzhou 730000, China

Abstract
HTML
Reference
Related

PDF

Abstract：
Irradiation of 110keV proton beam with exposure ranging from 1.0×10¹¹to 1.0×10¹⁷p/cm² onto the thermal control coatings of 6 different materials was performed, the changes of thermal properties were investigated and the surface chemical structure was analyzed by X-ray photoelectron spectroscopy XPS. It showed that the thermal properties of all the specimens was no obvious change and the surface chemical structure such as the chemical shift and elemental ratios changed little with the proton exposure less than 1.0×10¹⁴p/cm².Nevertheless, the thermal properties and surface chemical structure changed significantly with the proton exposure over 1.0×10¹⁴p/cm², for all the specimens the elemental ratio of C increased while the element ration of O decreased on the other hand. It is revealed that the proton irradiation with proper energy and fluence could improve the thermal properties of some thermal control coating of low solar absorptance.The changes both of the physics property and the surface chemical structure of the thermal control coatings resulting from the proton irradiation took place in phase.

References

[1]

. Silverman EM. Space Environmental Effects on Spacecraft:LEO Materials Selection Guide, NASA Contractor Report46612. Grossman E, Gouzman I. Nuclear Instruments in PhysicsResearch, 2003, B208: 48—573. WEN W X, YANG S S, WANG L. HEP NP, 2006, 30:268. (in Chinese)(文万信，杨生胜，王立.高能物理与核物理，2006, 30: 268)4. Ariza M J, Martin F, Leinen D. Applied Phys., 2001, A73:579—5845. Watts J F, Wolstenholme J. An Introduction to SurfaceAnalysis by XPS and AES. John Wiley Sons, 20026. EktessabiU A M, Hakamata S. Thin Solid Films, 2000,377—378: 621—625

[1]	HUANG Xiao-Long , JIANG Li-Yang , CHEN Xiong-Jun , CHEN Guo-Chang . Evaluation of the 1077 keV γ-ray emission probability from ⁶⁸Ga decay. Chinese Physics C, 2014, 38(4): 044001. doi: 10.1088/1674-1137/38/4/044001
[2]	ZHENG Lei , ZHAO Yi-Dong , TANG Kun , MA Chen-Yan , HAN Yong , CUI Ming-Qi . Total electron yield mode for XANES measurements in the energy region of 2.1--6.0 keV. Chinese Physics C, 2011, 35(2): 199-202. doi: 10.1088/1674-1137/35/2/018
[3]	ZHU Sheng-Jiang , WANG Jian-Guo , CHE Xing-Lai , DING Huai-Bo , XU Qiang , GU Long , YANG Yun-Yi . Search for chiral bands in A~110 neutron-rich nuclei. Chinese Physics C, 2009, 33(S1): 145-147. doi: 10.1088/1674-1137/33/S1/046
[4]	WEI Kong-Fang , WANG Zhi-Guang , LIU Chun-Bao , ZANG Hang , YAO Cun-Feng , SHENG Yan-Bin , MA Yi-Zhun , SONG Yin , LU Zi-Wei . Modification of Fe/Cu multilayers under 400 keV Xe²⁰⁺irradiation. Chinese Physics C, 2008, 32(S2): 262-264.
[5]	HAO Xin , ZHU Li-Hua , WU Xiao-Guang , HE Chuang-Ye , LI Guang-Sheng , LI Xue-Qin , LIU Ying , LI Li-Hua , PAN Bo . High-spin states and signature inversion studies in ¹¹⁰Ag. Chinese Physics C, 2008, 32(S2): 143-145.
[6]	LI Rui-Qi , LI Chun-Dong , HE Shi-Yu , DI Ming-Wei , YANG De-Zhuang . Energy Transfer of keV Proton in Kapton/Al. Chinese Physics C, 2007, 31(1): 114-118.
[7]	WANG Yi , KANG Ke-Jun , CHENG Jian-Ping , LI Yuan-Jing , LI Yang , LAI Yong-Fang , YUE Qian , LI Jin . Aging Test of Multi-gap Resistive Plate Chambers. Chinese Physics C, 2006, 30(5): 441-444.
[8]	WEN Wan-Xin , YANG Sheng-Sheng , WANG Li . Efsects of 110keV Proton Irradiation on Thermal Property of Themal Control Coatings. Chinese Physics C, 2006, 30(3): 268-272.
[9]	BAI Hong-Bo , ZHANG Jin-Fu , LI Yan-Song , ZHOU Xian-Rong , LIU Feng-Ying . E0 Transition as Another Indicator for Nuclear Shape Transitions and an Application to ^102—110Pd. Chinese Physics C, 2004, 28(3): 280-283.
[10]	ZHOU Chun-Mei . Calculation and Analysis of I_XK/I_γ(343keV)Ratio and Absolute Intensitiy Calculation of Radiation Data for ¹⁷⁵Hf Decay. Chinese Physics C, 2004, 28(8): 827-831.
[11]	YUAN Shi-Bin , WEI Zeng-Quan , LI Wen-Jian , GAO Qing-Xiang . Research on Molecular Modification of L(+)-Cysteine Induced by 110 keV Fe⁺ Ion Beam Irradiation. Chinese Physics C, 2003, 27(5): 460-464.
[12]	WANG Zhen-Xia , WANG Wen-Min , RUAN Mei-Ling . Formation of Boron Nitride Nanostructures by Means of 60keV N2+ Ion Beam Bombardment. Chinese Physics C, 2001, 25(2): 174-178.
[13]	LI Cheng , CHEN HongFang , WU Chong , ZHANG YongMing , XU ZiZong , LE Yi , SHAO ChuanFen , SHI ChangXin . Radiation Hardness Properties of MSM Structure Gallium Arsenide Detectors. Chinese Physics C, 2000, 24(5): 431-438.
[14]	Di Yaomin . Dynamical Correlation and the Collective States in ¹¹⁰Cd. Chinese Physics C, 1998, 22(2): 162-168.
[15]	Liu Changlong , Hou Mingdong , Wang Zhiguang , Cheng Song , Sun Youmei , Zhu Zhiyong , Jin Yunfan , Li Changlin , Wang Yinshu , Meng Qinghua . Dimensional Changes of Amorphous Alloys Under Swift Ar Ion Irradiation. Chinese Physics C, 1997, 21(11): 1052-1056.
[16]	Hou Mingdong , Liu Changlong , Quan Mingxiu , Sun Wensheng . Study of Topography Changes Induced by 150keV Argon Ion Bombardment of Amorphous Alloys. Chinese Physics C, 1994, 18(S1): 33-38.
[17]	XIANG Zheng-Yu , MU Yun-Shan , LI Ye-Xiang , WANG Shi-Ming , XU Hai-Shan . MEASUREMENTS OF NEUTRON CAPTURE CROSS SECTIONS OF WOLFRAM AND GADOLINIUM BETWEEN 560 AND 1610keV. Chinese Physics C, 1988, 12(1): 91-94.
[18]	WEI Kai-Yu , LIN Zhen-Hua . THE DESIGN AND STUDY OF SPACE CHARGE EFFECT FOR THE BPL 750keV BEAM TRANSPORT SYSTEM. Chinese Physics C, 1984, 8(5): 588-595.
[19]	CONG ZHI-BING , YU QING-CHANG , LI JI-GANG , LIANG JIA-MING , MA XING-HUA , LIU DIAN-KUI , LU HONG , XIA DE-HONG , SHU CHUAN-YU , ZHANG CAN-YING , LIU TIE-ZHU , YANG YOU-SHAN . DESIGN AND TESTS OF A PRESSURED "PIERCE" TYPE HIGH GRADIENT ACCELERATING TUBE OF 250 keV. Chinese Physics C, 1981, 5(6): 712-721.
[20]	. A HIGH GRADIENT 250keV PULSED PROTON BEAM ACCELERATING EQUIPMENT. Chinese Physics C, 1981, 5(6): 722-731.

Access

Get Citation

WEN Wan-Xin, YANG Sheng-Sheng and WANG Li. XPS Study of Property Changes of The Themal Control Coatings with 110keV Proton Irradiation[J]. Chinese Physics C, 2006, 30(4): 364-367.

WEN Wan-Xin, YANG Sheng-Sheng and WANG Li. XPS Study of Property Changes of The Themal Control Coatings with 110keV Proton Irradiation[J]. Chinese Physics C, 2006, 30(4): 364-367. shu

RIS(for EndNote,Reference Manager,ProCite)

BibTex

Txt

Milestone

Received: 2005-04-18
Revised: 1900-01-01

Article Metric

Article Views(3008)
PDF Downloads(587)
Cited by(0)

Policy on re-use

To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

XPS Study of Property Changes of The Themal Control Coatings with 110keV Proton Irradiation

Corresponding author: WEN Wan-Xin,

Department of Radiation Medicine, Soochow University, Suzhou 215007, China2 National Key Lab. of Vacuum & Cryogenics Technology and Physics, Lanzhou 730000, China

Received Date: 2005-04-18

Accepted Date: 1900-01-01

Available Online: 2006-04-05

Abstract: Irradiation of 110keV proton beam with exposure ranging from 1.0×10¹¹to 1.0×10¹⁷p/cm² onto the thermal control coatings of 6 different materials was performed, the changes of thermal properties were investigated and the surface chemical structure was analyzed by X-ray photoelectron spectroscopy XPS. It showed that the thermal properties of all the specimens was no obvious change and the surface chemical structure such as the chemical shift and elemental ratios changed little with the proton exposure less than 1.0×10¹⁴p/cm².Nevertheless, the thermal properties and surface chemical structure changed significantly with the proton exposure over 1.0×10¹⁴p/cm², for all the specimens the elemental ratio of C increased while the element ration of O decreased on the other hand. It is revealed that the proton irradiation with proper energy and fluence could improve the thermal properties of some thermal control coating of low solar absorptance.The changes both of the physics property and the surface chemical structure of the thermal control coatings resulting from the proton irradiation took place in phase.

HTML

Reference (1)

XPS Study of Property Changes of The Themal Control Coatings with 110keV Proton Irradiation

Abstract：

References

Access

Article Metrics

Metrics

通讯作者: 陈斌, bchen63@163.com

Email This Article